CoroMill® Plura lollipop för profilfräsning i ISO S
För svåråtkomliga detaljer
Performance test: Titanium
| Material: | S4.2.Z.AN (Ti64Al4V) |
| Operation: | Side milling |
| Coolant: | Emulsion |
+76%
Total machined surface
Total machined surface
|
| Competitor | Sandvik Coromant |
|---|---|---|
| Tool | Lollipop end mill (Z4) | 2L466-1000-TA1600 T2CH (Z6) |
| vc m/min (ft/min) | 375 (1230) | 375 (1230) |
| fn mm/rev (in/rev) | 0.045 (0.002) | 0.045 (0.002) |
| ae mm (inch) | 0.3 (0.012) | 0.3 (0.012) |
| ap mm (inch) | 0.1 (0.004) | 0.1 (0.004) |
| Tilt angle (°) | 12 | 12 |
| Tool life, min | 300 | 352 |
Resultat: CoroMill® Plura lollipop uppvisade 17 % längre livslängd i minuter med 76 % ökning i totalt bearbetad yta.
Totalt bearbetad yta
(konkurrent/Sandvik Coromant)
Konkurrent, 120 min
Sandvik Coromant, 120 min
Performance test, HRSA
| Material: | S2.0.Z.AG (aged inconel 718) |
| Operation: | Side milling |
| Coolant: | Emulsion |
+167%
Total remachined surface
Total remachined surface
|
| Competitor | Sandvik Coromant |
|---|---|---|
| Tool | Lollipop end mill (Z4) | 2L466-1000-RA1600 R2AH (Z6) |
| vc m/min (ft/min) | 100 (328) | 100 (328) |
| fn mm/rev (in/rev) | 0.025 (0.001) | 0.025 (0.001) |
| ae mm (inch) | 0.3 (0.012) | 0.3 (0.012) |
| ap mm (inch) | 0.1 (0.004) | 0.1 (0.004) |
| Tilt angle (°) | 12 | 12 |
| Tool life, min | 50 | 89 |
Resultat: CoroMill® Plura lollipop uppvisade 78 % längre livslängd i minuter med 167 % ökning i totalt bearbetad yta.
Totalt bearbetad yta
(konkurrent/Sandvik Coromant)
Konkurrent, 50 min
Sandvik Coromant, 50 min